EPOXY RESIN 4 WOOD ROT REPAIR & CRACK SEALING -BOAT DECK FIBERGLASSING RESIN

Description: AIR BUBBLE REMOVAL TECHNIQUEHOW TO REMOVE AIR BUBBLES FROM AN APPLIED EPOXY COATING, ALSO HELPS WITH LEVELING AND FLOW - YouTubeVideo will open in a new window FIBERGLASSING WITH MAX PCR A/BMAX PCR A/B works well as a laminating resin for composite fabrics such as fiberglass, carbon fiber, Aramid fiber and other hybrid and synthetic fabrics. Please review the COMPOSITE FABRICATING BASICS posted below. Apply a thin layer of the mixed MAX PCR A/B onto the prepared substrate to be reinforced. Apply a layer of fiberglass and aide the resin to wet-out the fiberglass using a brush and apply subsequent layers of fabric sandwiching a layer of resin until the desire thickness is achieved. Use a rubber squeegee to remove excess resin.Allow curing for 24 hours. BASIC EPOXY FIBERGLASS LAY UP TECHNIQUEVideo will open in a new windowAVAILABLE FIBERGLASS, CARBON FIBER, AND KEVLAR FABRICS FIBERGLASS PLAIN WEAVE 1.5-OUNCE HEXCEL 120 - 5 YARDS https://www.ebay.com/itm/222623985867 FIBERGLASS PLAIN WEAVE 1.5-OUNCE HEXCEL 120 -10 YARDS https://www.ebay.com/itm/311946399588 FIBERGLASS PLAIN WEAVE 7.0-OUNCE HEXCEL 7532 -5 YARDS https://www.ebay.com/itm/222624899999 FIBERGLASS PLAIN WEAVE 10-OUNCE STYLE 1800 -3 YARDS https://www.ebay.com/itm/223496626702 FIBERGLASS PLAIN WEAVE 10-OUNCE STYLE 1800 -5 YARDS https://www.ebay.com/itm/223495621157 FIBERGLASS SATIN WEAVE 9.0 -OUNCE HEXCEL 7781 -5 YARDS https://www.ebay.com/itm/223508087559 FIBERGLASS SATIN WEAVE 26 OUNCE HEXCEL 1584 -3 YARDS https://www.ebay.com/itm/311947365010 FIBERGLASS SATIN WEAVE 26 OUNCE HEXCEL 1584 -5 YARDS https://www.ebay.com/itm/222629157570 CARBON FIBER FABRIC 3K 2x2 TWILL WEAVE 6 OZ -3 YARDS https://www.ebay.com/itm/311947275431 CARBON FIBER FABRIC 3K PLAIN WEAVE 6-OZ -3 YARDS https://www.ebay.com/itm /311947292012 KEVLAR 49 HEXCEL 351 PLAIN WEAVE FABRIC 2.2 OZ https://www.ebay.com/itm/222623951106 CleanupUse up all mixed resin or discard properly. Clean the equipment and other processing implements with acetone or equivalent solvents immediately after use. ADDING COLOR WITHMAX COLOR PIGMENT CONCENTRATESThese are color concentrates only and must be dispersed an epoxy resin or PART A component. These color concentrates are used to blend in with MAX GPE COLORED EPOXY SYSTEM to attain other colors or to intensify color opacity.MAX COLOR KIT https://www.ebay.com/itm/311946633043Addition of color will also increase UV durability of the coating. Color Addition ProcedureVideo will open in a new window ******************************************************** COMPOSITE FABRICATING BASIC GUIDELINESA fabricated COMPOSITE material is a manufactured collection of two or more ingredients or products intentionally combined to form a new homogeneous material that is defined by its performance that should uniquely greater than the sum of its individual parts. This method is also defined as a SYNERGISTIC COMPOSITION. COMPOSITE MATERIAL COMPOSITIONREINFORCING FABRIC & IMPREGNATING RESIN PLUS 'ENGINEERED PROCESS' EQUALS COMPOSITE LAMINATE WITH THE BEST WEIGHT TO STRENGTH PERFORMANCE With respect to the raw materials selection -fabric and resin, the fabricating process and the and curing and test validation of composite part, these aspects must be carefully considered and in the engineering phase of the composite. Step One: Fabric SelectionTYPES OF FABRIC WEAVE STYLE AND SURFACE FINISHINGFOR RESIN TYPE COMPATIBILITY Fabrics are generally considered ”balanced” if the breaking strength is within 15% warp to fill and are best in bias applications on lightweight structures. “Unbalanced” fabrics are excellent when a greater load is required one direction and a lesser load in the perpendicular direction. Tow: The bundle of individual carbon filaments used to weave carbon fabric. 50k tow means there are 48-50,000 carbon filaments in the tow. Smaller tow i.e. 12k, 6k, 3k and 1k are obtained by dividing the 50k tow into smaller bundles.Thread Count: The number of threads (tow in carbon and yarn in Aramid) per inch. The first number will be the warp count and the second will be the fill count. Fill: The threads that run the width of the roll or bolt and perpendicular to the warp threads. Warp: The threads that run the length of the roll or bolt and perpendicular to the fill threads. Finish: The chemical treatment to fiberglass making it compatible with resin systems, therefore improving the bond between the fiber and the resin. Finishing fiberglass typically decreases the fiber strength by as much as 50%. Both Silane and Volan finishes are epoxy compatible. Historically, Volan has been considered a softer finish for a more pliable fabric, but recent advances have yielded some excellent soft Silane finishes.Thickness: Measured in fractions of an inch. The thicker the fabric the more resin required to fill the weave to obtain a surface-smooth finished part.Weaves:Plain weave means the warp and fill threads cross alternately. This is the most common weave.4 Harness (4 HS Satin or crowfoot) weave means the fill thread floats over three warp threads, then under one warp thread. This weave is more pliable than the plain weave, therefore conforms to complex curves more easily.8 Harness (8 HS Satin) weave means the fill thread floats over seven warp threads, then under one warp thread. This weave is the most pliable of the standard fiberglass weaves.2 x 2 Twill weave means the fill thread floats over two warp threads, then fewer than two warp threads. This weave is found most commonly in carbon fabrics and is more pliable than plain weave.Most fabrics are stronger in the warp than the fill because higher tension is placed on the warp fiber keeping it straighter during the weaving process. Rare exceptions occur when a larger, therefore stronger thread is used in the fill direction than the warp direction. PLAIN WEAVE Is a very simple weave pattern and the most common style. The warp and fill yarns are interlaced over and under each other in alternating fashion. Plain weave provides good stability, porosity and the least yarn slippage for a given yarn count.8 HARNESS SATIN WEAVE The eight-harness satin is similar to the four-harness satin except that one filling yarn floats over seven warp yarns and under one.This is a very pliable weave and is used for forming over curved surfaces.4 HARNESS SATIN WEAVEThe four-harness satin weave is more pliable than the plain weave and is easier to conform to curved surfaces typical in reinforced plastics. In this weave pattern, there is a three by one interfacing where a filling yarn floats over three warp yarns and under one.2x2 TWILL WEAVETwill weave is more pliable than the plain weave and has better drivability while maintaining more fabric stability than a four or eight harness satin weave. The weave pattern is characterized by a diagonal rib created by one warp yarn floating over at least two filling yarns.Plain Weaves, Bi-axial, Unidirectional Styles For Directional High Strength Parts Use this weave style cloth when high strength parts are desired.It is ideal for reinforcement, mold making, aircraft and auto parts tooling, marine, and other composite lightweight applications. Click The Image To View Video7544 Fiberglass - YouTube AVAILABLE FABRICS FIBERGLASS, CARBON FIBER, AND KEVLAR FABRICS FIBERGLASS PLAIN WEAVE 1.5-OUNCE HEXCEL 120 - 5 YARDS https://www.ebay.com/itm/222623985867 FIBERGLASS PLAIN WEAVE 1.5-OUNCE HEXCEL 120 -10 YARDS https://www.ebay.com/itm/311946399588 FIBERGLASS PLAIN WEAVE 7.0-OUNCE HEXCEL 7532 -5 YARDS https://www.ebay.com/itm/222624899999 FIBERGLASS PLAIN WEAVE 10-OUNCE STYLE 1800 -3 YARDS https://www.ebay.com/itm/223496626702 FIBERGLASS PLAIN WEAVE 10-OUNCE STYLE 1800 -5 YARDS https://www.ebay.com/itm/223495621157 FIBERGLASS SATIN WEAVE 9.0 -OUNCE HEXCEL 7781 -5 YARDS https://www.ebay.com/itm/223508087559 FIBERGLASS SATIN WEAVE 26 OUNCE HEXCEL 1584 -3 YARDS https://www.ebay.com/itm/311947365010 FIBERGLASS SATIN WEAVE 26 OUNCE HEXCEL 1584 -5 YARDS https://www.ebay.com/itm/222629157570 CARBON FIBER FABRIC 3K 2x2 TWILL WEAVE 6 OZ -3 YARDS https://www.ebay.com/itm/311947275431 CARBON FIBER FABRIC 3K PLAIN WEAVE 6-OZ -3 YARDS https://www.ebay.com/itm /311947292012 KEVLAR 49 HEXCEL 351 PLAIN WEAVE FABRIC 2.2 OZ https://www.ebay.com/itm/222623951106 Step Two: Choose The Best Epoxy Resin System For The ApplicationThe epoxy resin used in fabricating a laminate will dictate how the FRP will perform when load or pressure is implied on the part.To choose the proper resin system, consider the following factors that are crucial to a laminate's performance.SIZE AND CONFIGURATION OF THE PART(NUMBER OF PLIES AND CONTOURED, FLAT OR PROFILED)CONSOLIDATING FORCE(FREE STANDING DRY OR HAND LAY-UP, VACUUM BAG OR PLATEN PRESS CURING)CURING CAPABILITIES(HEAT CURED OR ROOM TEMPERATURE CURED)LOAD PARAMETERS(SHEARING FORCE, TORSIONAL AND DIRECTIONAL LOAD, BEAM STRENGTH)ENVIRONMENTAL EXPOSURE The principal role of the resin is to bind the fabric into a homogeneous rigid substrate(OPERATING TEMPERATURE, AMBIENT CONDITIONS, CHEMICAL EXPOSURE, CYCLIC FORCE LOADING) MATERIAL AND PRODUCTION COST(BUYING IN BULK WILL ALWAYS PROVIDE THE BEST OVERALL COSTS) These factors will dictate the design and the composition of the part and must be carefully considered during the design and engineering phase of the fabrication. TOP SELLING IMPREGNATING RESIN SYSTEM MAX BOND LOW VISCOSITY A/BMarine Grade Boat Building Resin System, Fiberglassing/Impregnating, Water Resistance, Cured Structural StrengthMAX BOND LOW VISCOSITY 32-Ounce kit https://www.ebay.com/itm/311947109148MAX BOND LOW VISCOSITY 64-Ounce Kit https://www.ebay.com/itm/311947125422MAX BOND LOW VISCOSITY 1-Gallon Kit https://www.ebay.com/itm/311947117608MAX BOND LOW VISCOSITY 2-Gallon kit https://www.ebay.com/itm/311946370391 MAX BOND LOW VISCOSITY 10-Gallon Kit https://www.ebay.com/itm/222624960548MAX 1618 A/B Crystal Clear, High Strength, Lowest Viscosity (Thin) Excellent For Woodworking And FiberglassingMAX 1618 A/B 48-Ounce Kit https://www.ebay.com/itm/222627258390MAX 1618 A/B 3/4-Gallon Kit https://www.ebay.com/itm/222625113128MAX 1618 A/B 3/4-Gallon Kit https://www.ebay.com/itm/222627258390 MAX 1618 A/B 1.5-Gallon Kit https://www.ebay.com/itm/311946441558MAX CLR A/B FDA Compliant For Food Contact, High Impact, Low Viscosity, Water Clear Transparency, Chemical Resistance,MAX CLR A/B 24-Ounce Kit https://www.ebay.com/itm/222623963194MAX CLR A/B 48-Ounce Kit https://www.ebay.com/itm/311947320101MAX CLR A/B 96-Ounce Kit https://www.ebay.com/itm/222625329068MAX CLR A/B 96-Ounce Kit https://www.ebay.com/itm/222625338230 MAX CLR A/B 1.5-Gallon Kit https://www.ebay.com/itm/222626972426 MAX GRE A/B GASOLINE RESISTANT EPOXY RESINResistant To Gasoline/E85 Blend, Acids & Bases, Sealing, Coating, Impregnating ResinMAX GRE A/B 48-Ounce Kit:https://www.ebay.com/itm/311946473553MAX GRE A/B 96-Ounce Kit:https://www.ebay.com/itm/311947247402MAX HTE A/B HIGH-TEMPERATURE EPOXYHeat Cured Resin System For Temperature Resistant Bonding, Electronic Potting, Coating, BondingMAX HTE A/B 80-Ounce Kit https://www.ebay.com/itm/222624247814MAX HTE A/B 40-Ounce Kit https://www.ebay.com/itm/222624236832Step Three:Proper Lay-Up Technique -Putting It All TogetherPre-lay-up notesLay out the fabric and pre-cut to size and set asideAvoid distorting the weave pattern as much as possibleFor fiberglass molding, ensure the mold is clean and adequate mold release is usedView our video presentation above "MAX EPOXY RESIN MIXING TECHNIQUE"Mix the resin only when all needed materials and implements needed are ready and within reachMix the proper amount of resin needed and be accurate proportioning the resin and curing agent. Adding more curing agent than the recommended mix ratio will not promote a faster cure. Over saturation or starving the fiberglass or any composite fabric will yield poor mechanical performance. When mechanical load or pressure is applied to the composite laminate, the physical strength of the fabric should bear the stress and not the resin. If the laminate is over saturated with the resin it will most likely to fracture or shatter instead of rebounding and resist damage.Don’t how much resin to use to go with the fiberglass?A good rule of thumb is to maintain a minimum of 30 to 35% resin content by weight, this is the optimum ratio used in high-performance prepreg (or pre-impregnated fabrics) typically used in aerospace and high-performance structural application.For general hand lay-ups, calculate using 60% fabric weight to 40% resin weight as a safety factor. This will ensure that the fabricated laminate will be below 40% resin content depending on the waste factor accrued during fabrication.Place the entire pre-cut fiberglass to be used on a digital scale to determine the fabric to resin weight ratio. Measuring by weight will ensure accurate composite fabrication and repeatability, rather than using OSY data.THE USE OF A WEIGHING SCALE IS HIGHLY RECOMMENDED Purchase this scale with any of our product offering and the shipping cost of the scale is freehttps://www.ebay.com/itm/222630300203A good rule of thumb is to maintain a minimum of 30 to 35% resin content by weight, this is the optimum ratio used in high-performance prepreg (or pre-impregnated fabrics) typically used in aerospace and high-performance structural application. For general hand lay-ups, calculate using 60% fabric weight to 40% resin weight as a safety factor. This will ensure that the fabricated laminate will be below 40% resin content depending on the waste factor accrued during fabrication.Place the entire pre-cut fiberglass to be used on a digital scale to determine the fabric to resin weight ratio. Measuring by weight will ensure accurate composite fabrication and repeatability, rather than using OSY data.Typical fabric weight regardless of the weave pattern 1 ounce per square yard is equal to 28.35 grams 1 square yard equals to 1296 square inches (36 inches x 36 inches) FOR EXAMPLE 1 yard of 10-ounces per square yard (OSY) fabric weighs 283 grams. Ounces per square yard or OSY is also known as aerial weight, which is the most common unit of measurement for composite fabrics. To determine how much resin is needed to adequately impregnate the fiberglass, use the following equation: (Total Weight of Fabric divided by 60%)X( 40%)= weight of mixed resin needed OR fw= fabric weight rc= target resin content rn=resin needed MASTER EQUATION (fw/60%)x(40%)=rn GENERAL LAY-UP PROCEDUREApply the mixed resin onto the surface and then lay the fabric and allow the resin to saturate through the fabric.NOT THE OTHER WAY AROUNDThis is one of the most common processing error that yields sub-standard laminates. By laying the fiberglass onto a layer of the prepared resin, fewer air bubbles are entrapped during the wetting-out stage. Air is pushed up and outwards instead of forcing the resin through the fabric which will entrap air bubbles. This technique will displace air pockets unhindered and uniformly disperse the impregnating resin throughout the fiberglass.HAND LAY-UP TECHNIQUE Eliminating air entrapment or void porosity in an epoxy/fiberglass lay-up processFiberglass Hand Lay Up For Canoe and Kayak BuildingVideo will open in a new windowBasic Hand Lay-up FiberglassingVideo will open in a new windowVACUUM BAGGING PROCESS For performance critical application used in aerospace vehicles, composite framing for automotive vehicles and marine vessels, a process called 'Vacuum Bagging' is employed to ensure the complete consolidation of every layer of fabric. The entire tooling and lay-up are encased in an airtight envelope or bagging and a high-efficiency vacuum pump is used to draw out the air within the vacuum bag to create a negative atmospheric pressure. Once a full vacuum (29.9 Inches of Mercury) is achieved, the negative pressure applies a compacting force of 14.4 pounds per square inch (maximum vacuum pressure at sea level) is applied to the vacuum bag transferring the force to the entire surface area of the laminate. Vacuum pressure is maintained until the resin cures to a solid. For room temperature curing resin system, the vacuum pump is left in operation for a minimum of 18 hours. External heat can be applied to the entire lay-up, thus accelerating the cure of the resin system. The vacuum force also removes any entrapped air bubble between the layers of fabric and eliminate what is called, porosity or air voids. Porosity within a laminate creates weak spots in the structure that can be the source of mechanical failure when force or load is applied to the laminate. The standard atmosphere (symbol: atm) is a unit of pressure defined as 1 01325 Pa (1.01325 bar), equivalent to 760 mm Mercury or 29.92 inches Mercury or 14.696 pounds per square inch of pressure.Fiberglass And Carbon Fiber Vacuum BaggingVideo will open in a new window AUTOCLAVE CURING PROCESS Autoclave curing processing is the most common method used in large-scale production of composite products. The Aerospace Industry, which includes space exploration rockets and vehicles, deep space structures, and commercial and military airplane utilizes this composite fabrication process due to the critical nature of the application. The mechanical demands of the composite are often pushed to the upper limits and autoclaved process yields composites with the best weight to strength ratio.BASIC OPERATION OF THE AUTOCLAVE PROCESS In the autoclave process, high pressure and heat are applied to the part through the autoclave atmosphere, with a vacuum bag used to apply additional pressure and protect the laminate from the autoclave gases. The cure cycle for a specific application is usually determined empirically and, as a result, several cure cycles may be developed for a single material system, to account for differences in laminate thickness or to optimize particular properties in the cured part.The typical autoclave cure cycle is a two-step process. First, vacuum and pressure are applied while the temperature is ramped up to an intermediate level and held there for a short period of time. The heat reduces the resin viscosity, allowing it to flow and making it easier for trapped air and volatiles to escape. The resin also begins wetting the fibers at this stage.In the second ramp up, the temperature is raised to the final cure temperature and held for a sufficient length of time to complete the cure reaction. During this step, the viscosity continues to drop, but preset temperature ramp rates and hold times then stabilize viscosity at a level that permits adequate consolidation and fiber wetting, while avoiding excessive flow and subsequent resin starvation. These control factors also slow the reaction rate, which prevents excessive heat generation from the exothermic polymerization process. Upon completion, the cured mechanical performance of the composite is often much stronger and lighter compared to a hand lay-up, or vacuum bagged composite laminate. VACUUM INFUSION PROCESSVacuum Infusion Process is also known in the composites industry as Vacuum Assisted Resin Transfer Molding or VARTM.Similar to the Vacuum Bagging Process where the negative pressure is used to apply consolidation force to the laminate while the resin cures, the resin is infused into the fabric lay-up by sucking the impregnating resin and thus forming the composite laminate.The VARTM Process produces parts that require less secondary steps, such as trimming, polishing or grinding with excellent mechanical properties. However, the vacuum infusion requires more additional or supplemental related equipment and expendable materials. So the pros and cons of each presented composite fabrication process should be carefully determined to suit the user's capabilities and needs.Please view the following video demonstration which explains the process of Vacuum Infusion or VARTM process.MAX 1618 A/B VACUUM ASSISTED RESIN TRANSFER MOLDING PROCESSCARBON FIBER VACUUM INFUSION WITH MAX 1618Video will open in a new window Step Four: Proper CuringAlthough we have formulated all of our MAX EPOXY RESIN SYSTEM product line to be resistant to amine-blush,it is recommended not to mix any resin systems in high humidity conditions, greater than 60%.Always make sure that the substrate or material the epoxy resin system is being applied to is well prepared as possible to ensure the best-cured performance. Always review the published data and information for proper usage, application, and general safety information. Our expert staff of engineers is always available for consultation and assistance. Allow the lay-up to cure for a minimum of 24 to 36 hours before handling.Optimum cured properties can take up to 7 days depending on the ambient cure condition. The ideal temperature cure condition of most room temperature epoxy resin is 22 to 27 degrees Celsius at 20% relative humidity.Higher ambient curing temperatures will promote faster polymerization and development of cured mechanical properties.Improving mechanical performance via post heat cure A short heat post cure will further improve the mechanical performance of most epoxy resins. Allow the applied resin system to cure at room temperature until for 18 to 24 hours and if possible, expose heat cure it in an oven or other sources of radiant heat (220°F to 250°F) for 45 minute to an hour. You can also expose it to direct sunlight but place a dark colored cover, such as a tarp or cardboard to protect it from ultraviolet exposure.In general room temperature cured epoxy resin has a maximum operating temperature of 160°F or lower.A short heat post cure will ensure that the mixed epoxy system is fully cured,especially for room temperature cure system that can take up to 7 days to achieve 100% cureSome darkening or yellowing of the epoxy resin may occur if overexposed to high temperature (>250 F). AMINE BLUSHThe affinity of an amine compound (curing agent) to moisture and carbon dioxide creates a carbonate compound and forms what is called amine blush. Amine blush is a wax-like layer that forms as most epoxies cure. If the epoxy system is cured in extreme humidity (>70%).It will be seen as a white and waxy layer that must be removed by physical sanding of the surface followed by an acetone wipe. OTHER TYPES OF EPOXY RESIN CURE MECHANISMLATENT CURING SYSTEMSLatent epoxy resins are systems that are mixed together at room temperature and will begin polymerization but it will not achieve full cure unless it is exposed to a heat cure cycle. In general, these are high-performance systems that demonstrate exceptional performance under extreme conditions such as high mechanical performance under heat and cryogenic temperatures, chemical resistance or any environment that epoxy room temperature system perform marginally or poorly. Upon the mixing of the resin and curing agent polymerization will begin and will only achieve a partial cure. Some resins may appear cured or dry to the touch, this state is called 'B-Stage Cure', but upon application of force will either be gummy or brittle almost glass-like and will dissolve in most solvents. The semi-cured resin must be exposed to an elevated temperature for it to continue polymerization and achieve full cure. HEAT ACTIVATED CURING SYSTEMSThis type of epoxy system will not polymerize unless it is exposed to the activation temperature of the curing agent which can be as low as 200 deg F and as high as 400 deg F. In most instances, our MAX EPOXY SYSTEMS epoxy system can be stored at room temperature and remain liquid for up to six months and longer. TESTING THE FIBERGLASS LAMINATEDETERMINATION OF THE FABRIC-RESIN RATIO TESTING FABRIC TO RESIN RATIO VIA RESIN BURN OUTULTIMATE COMPRESSIVE STRENGTH ULTIMATE COMPRESSIVE STRENGTH TEST6500 Pounds To Failure / 0.498 Square Inch=13,052 psi Maximum Compressive StrengthSPECIMEN EXAMINATION AFTER COMPRESSION TEST**********************************************DON'T FORGET OUR EPOXY MIXING KITClick The Link To Add To Orderhttps://www.ebay.com/itm/222623932456EVERYTHING YOU NEED TO MEASURE, MIX, DISPENSE OR APPLY ANY OF OUR MAX EPOXY RESIN IN ONE CONVENIENT KITProportioning the correct amount is equally as important to attain the intended cured properties of the resin system.The container in which the epoxy and curing agent is mixed is an important consideration when mixing an epoxy resin system. The container must withstand the tenacity of the chemical and must be free of contamination.Most epoxy curing agent has a degree of corrosivity, as a general practice, protective gloves should be worn when handling chemicals of the same nature. MIXING KIT CONTENTS 4 each 32 ounce (1 Quart) clear HDPE plastic tubs4 each 16 ounce (1 pint) clear HDPE plastic tubs4 each clear HDPE Plastic Lids for the plastic tubs4 each 8 ounce (1/2-Pint) Wax Free Paper Cups5 pairs one size fits all Powder-Free Latex Gloves (Large)6 Piece HDPE Plastic Measuring Spoon Kit(1 tablespoon to 1/8 teaspoon)10 Piece HDPE Plastic Measuring Cup(1 Cup to 1/8 Teaspoon)2 each None Sterile Graduated 10 cc Syringes1 pack of Wooden Stir Sticks (Disposable Chopsticks)1 pack Assorted Size Bristle Brush (5 per pack) PLEASE CHECK OUT OTHER AVAILABLERESIN SYSTEMS AT OUR eBay STOREFor our complete listing, please Visit our eBay store! IMPORTANT NOTICEYour purchase constitutes the acceptance of this disclaimer. Please review before purchasing this product. The user should thoroughly test any proposed use of this product and independently conclude satisfactory performance in the application. Likewise, if the manner in which this product is used requires government approval or clearance, the user must obtain said approval. The information contained herein is based on data believed to be accurate at the time of publication. Data and parameters cited have been obtained through published information, PolymerProducts laboratories using materials under controlled conditions. Data of this type should not be used for a specification for fabrication and design. It is the user's responsibility to determine this Composites fitness for use. There is no warranty of merchantability of fitness for use, nor any other express implied warranty. The user's exclusive remedy and the manufacturer's liability are limited to refund of the purchase price or replacement of the product within the agreed warranty period. PolymerProducts and its direct representative will not be liable for incidental or consequential damages of any kind. Determination of the suitability of any kind of information or product for the use contemplated by the user, the manner of that use and whether there is any infringement of patents is the sole liability of the user.

Price: 83.92 USD

Location: Ontario, California

End Time: 2024-01-15T00:51:26.000Z

Shipping Cost: 0.72 USD